35Mn簡介
China GBT Structure Steel 35Mn，及該型號鋼材的基本信息、化學(xué)元素成分、機械性能、力學(xué)性能、熱處理溫度、同等型號參照表等。
基本信息：
| 分類 |
種類 |
型號 |
標準 |
國家 |
應(yīng)用 |
|---|
| Steel Grades |
|
35Mn |
GBT |
China |
China structural steel and alloy steel |
化學(xué)成分信息(mass fraction)(wt.%) of the 35Mn：
| 元素名稱 |
含量比例值 |
|---|
| C |
0.32-0.39 |
| Si |
0.17-0.37 |
| Mn |
0.70-1.00 |
| P |
0.035 |
| S |
0.035 |
| Cr |
0.25 |
| Ni |
0.3 |
機械性能信息：
| 屈服強度Rp0.2（MPa） |
抗拉強度Rm（MPa） |
沖擊率 |
伸長率 |
斷面收縮率 |
熱處理狀態(tài) |
布氏硬度（HBW） |
|---|
| 755 (≥) |
728 (≥) |
41 |
32 |
31 |
Solution and Aging, Annealing, Ausaging, Q+T,etc |
442 |
物理性質(zhì)信息：
| 溫度 |
彈性模量 |
系數(shù) |
熱導(dǎo)率 |
比熱容量 |
比電阻率 |
密度 |
加權(quán)系數(shù) |
|---|
| 33 |
- |
- |
|
|
0.43 |
- |
|
| 919 |
689 |
- |
14.3 |
312 |
|
- |
|
| 335 |
- |
13 |
33.2 |
|
|
142 |
213 |
熱處理信息：
| 熱處理溫度區(qū)間 |
|---|
| Heat treated : 1578°C - 1742°C |
對照表（同等等級）信息：
| 型號 |
標準 |
國家 |
應(yīng)用 |
|---|
| CK-35MN |
ASTM |
USA |
Castings, Iron-Chromium, Iron-Chromium-Nickel, Corrosion Resistant, for General Application |
| 35Mn14 |
STAS/SR |
Romania |
Structural steel |
| 35Mn16 |
STAS/SR |
Romania |
Structural steel |
| 35MnSi13 |
STAS/SR |
Romania |
Alloy structural steel |
| 35MnSi13X |
STAS/SR |
Romania |
Alloy structural steel |
| 35MnSi13XS |
STAS/SR |
Romania |
Alloy structural steel |
| 35Mn |
GBT |
China |
China structural steel and alloy steel |
| YF35MnV |
GBT |
China |
China structural steel and alloy steel |
| F35MnVN |
GBT |
China |
China structural steel and alloy steel |
| 35Mn2 |
GBT |
China |
China structural steel and alloy steel |
| ML35Mn |
GBT |
China |
China structural steel and alloy steel |
| ML35MnB |
GBT |
China |
China structural steel and alloy steel |
| ZG35Mn(ZG35SiMn) |
GBT |
China |
Large castings with low alloy cast steel |
| CK-35MN |
ASTM |
USA |
Castings, Iron-Chromium, Iron-Chromium-Nickel, Corrosion Resistant, for General Application |
| CK-35MN |
ASTM |
USA |
Castings, Iron-Chromium, Iron-Chromium-Nickel, Corrosion Resistant, for General Application |